長(zhǎng)期供應(yīng)四氟乙稀共聚物ETFE塑膠原料
Tefzel? 2195 物性表
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 額定值 | 單位制 | 測(cè)試方法 |
|---|---|---|---|
| 比重 | 1.72 | g/cm3 | ASTM D792 |
| 表觀密度 | 0.75 | g/cm3 | 內(nèi)部方法 |
| 熔流率（熔體流動(dòng)速率）?(297°C/5.0 kg) | 20 | g/10 min | ASTM D3159 |
| 吸水率?(24 hr) | < 0.030 | % | ASTM D570 |
| 平均顆粒尺寸 | 270 | μm |
| 熱性能 | 額定值 | 單位制 | 測(cè)試方法 |
|---|---|---|---|
| 高使用溫度?1 | 150 | °C | |
| 熔融溫度 | 253 | °C | ASTM D3418 |
| 線形熱膨脹系數(shù) - 流動(dòng)?(0 到 100°C) | 9.0E-5 | cm/cm/°C | ASTM D696 |
| 備注 | |
|---|---|
| 1 . | The upper service temperature is based on heat-aging tests and represents the temperature at which tensile strength and elongation would be expected to be diminished 50% after 10,000 hr thermal aging. Upper service temperatures above 150°C (302°F) may be feasible, depending on such factors as chemical exposure and support from the substrate. Particularly when considering uses of Tefzel ? 2195 above 150°C (302°F), perform preliminary testing to verify the acceptability. |
免責(zé)聲明：（1）以上所展示的信息由企業(yè)自行提供，內(nèi)容的真實(shí)性、準(zhǔn)確性和合法性由發(fā)布企業(yè)負(fù)責(zé)，環(huán)球塑化網(wǎng)對(duì)此不承擔(dān)任何保證責(zé)任。我們?cè)瓌t上建議您優(yōu)先選擇“塑企通”會(huì)員合作! （2）同時(shí)我們鄭重提醒各位買/賣家，交易前請(qǐng)?jiān)敿?xì)核實(shí)對(duì)方身份，切勿隨意打款或發(fā)貨，謹(jǐn)防上當(dāng)受騙。如發(fā)現(xiàn)虛假信息，請(qǐng)向環(huán)球塑化網(wǎng)舉報(bào)。