| DuPont Performance Polymers Zytel? HTN92G35DH2 BK083 PA6T/66-GF35 | |||
|---|---|---|---|
| Categories: | Polymer; Thermoplastic; Polyphthalamide (PPA); Polyphthalamide (PPA), 40% Glass Fiber Reinforced | ||
| Material Notes: |
35% Glass Reinforced, PPA, High Performance Polyamide with DuPont
Information provided by DuPont Performance Polymers |
||
| Vendors: |
Click here to view all available suppliers for this material. Please click here if you are a supplier and would like information on how to add your listing to this material. |
||
|
|||
Printer friendly version
Download as PDF
Download to Excel (requires Excel and Windows)
Export data to your CAD/FEA program| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in3 | DAM; ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.00200 cm/cm | 0.00200 in/in | DAM; ISO 294-4, 2577 | ||
| 0.00900 cm/cm | 0.00900 in/in | DAM; ISO 294-4, 2577 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 157 MPa | 22800 psi | 50%RH; ISO 527-1/-2 | ||
| 200 MPa | 29000 psi | DAM; ISO 527-1/-2 | |||
| Elongation at Break | 2.40 % | 2.40 % | DAM; ISO 527-1/-2 | ||
| 2.60 % | 2.60 % | 50%RH; ISO 527-1/-2 | |||
| Tensile Modulus | 10.0 GPa | 1450 ksi | 50%RH; ISO 527-1/-2 | ||
| 12.0 GPa | 1740 ksi | DAM; ISO 527-1/-2 | |||
|
3.226 GPa @Temperature 230 °C |
467.9 ksi @Temperature 446 °F |
DAM; ISO 11403-1,-2 | ||
|
4.312 GPa @Temperature 200 °C |
625.4 ksi @Temperature 392 °F |
DAM; ISO 11403-1,-2 | |||
|
4.575 GPa @Temperature 150 °C |
663.5 ksi @Temperature 302 °F |
50%RH; ISO 11403-1,-2 | |||
|
4.902 GPa @Temperature 150 °C |
711.0 ksi @Temperature 302 °F |
DAM; ISO 11403-1,-2 | |||
|
5.809 GPa @Temperature 90.0 °C |
842.5 ksi @Temperature 194 °F |
50%RH; ISO 11403-1,-2 | |||
|
6.624 GPa @Temperature 90.0 °C |
960.7 ksi @Temperature 194 °F |
DAM; ISO 11403-1,-2 | |||
|
10.09 GPa @Temperature 23.0 °C |
1463 ksi @Temperature 73.4 °F |
50%RH; ISO 11403-1,-2 | |||
|
11.69 GPa @Temperature 23.0 °C |
1695 ksi @Temperature 73.4 °F |
DAM; ISO 11403-1,-2 | |||
|
11.84 GPa @Temperature -20.0 °C |
1717 ksi @Temperature -4.00 °F |
DAM; ISO 11403-1,-2 | |||
|
12.06 GPa @Temperature -20.0 °C |
1749 ksi @Temperature -4.00 °F |
50%RH; ISO 11403-1,-2 | |||
| Flexural Strength | 272 MPa | 39500 psi | DAM; ISO 178 | ||
| Flexural Modulus | 10.0 GPa | 1450 ksi | DAM; ISO 178 | ||
|
Charpy Impact Unnotched
|
4.50 J/cm2 @Temperature -30.0 °C |
21.4 ft-lb/in2 @Temperature -22.0 °F |
50%RH; ISO 179/1eU | ||
|
5.00 J/cm2 @Temperature 23.0 °C |
23.8 ft-lb/in2 @Temperature 73.4 °F |
50%RH; ISO 179/1eU | |||
|
5.00 J/cm2 @Temperature -30.0 °C |
23.8 ft-lb/in2 @Temperature -22.0 °F |
DAM; ISO 179/1eU | |||
|
5.50 J/cm2 @Temperature 23.0 °C |
26.2 ft-lb/in2 @Temperature 73.4 °F |
DAM; ISO 179/1eU | |||
|
Charpy Impact, Notched
|
1.00 J/cm2 @Temperature 23.0 °C |
4.76 ft-lb/in2 @Temperature 73.4 °F |
50%RH; ISO 179/1eA | ||
|
1.00 J/cm2 @Temperature -40.0 °C |
4.76 ft-lb/in2 @Temperature -40.0 °F |
50%RH; ISO 179/1eA | |||
|
1.00 J/cm2 @Temperature 23.0 °C |
4.76 ft-lb/in2 @Temperature 73.4 °F |
DAM; ISO 179/1eA | |||
|
1.00 J/cm2 @Temperature -40.0 °C |
4.76 ft-lb/in2 @Temperature -40.0 °F |
DAM; ISO 179/1eA | |||
| Tensile Creep Modulus, 1 hour | 10000 MPa | 1.45e+6 psi | 50%RH; ISO 899-1 | ||
| Tensile Creep Modulus, 1000 hours | 8500 MPa | 1.23e+6 psi | 50%RH; ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | 50%RH; IEC 60093 | ||
| >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | DAM; IEC 60093 | |||
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | 50%RH; IEC 60093 | ||
| Dielectric Strength | 32.0 kV/mm | 813 kV/in | DAM; IEC 60243-1 | ||
| Comparative Tracking Index | 600 V | 600 V | DAM; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 19.0 μm/m-°C | 10.6 μin/in-°F | DAM; ISO 11359-1/-2 | ||
|
19.0 μm/m-°C @Temperature -40.0 - 23.0 °C |
10.6 μin/in-°F @Temperature -40.0 - 73.4 °F |
DAM; ISO 11359-1/-2 | |||
| CTE, linear, Transverse to Flow | 63.0 μm/m-°C | 35.0 μin/in-°F | DAM; ISO 11359-1/-2 | ||
|
|
63.0 μm/m-°C @Temperature -40.0 - 23.0 °C |
35.0 μin/in-°F @Temperature -40.0 - 73.4 °F |
DAM; ISO 11359-1/-2 | ||
| Melting Point | 310 °C | 590 °F | first heat; DAM; ISO 11357-1/-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 283 °C | 541 °F | DAM; ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | >= 320 °C | >= 608 °F | |||
| 325 °C | 617 °F | Optimum | |||
| <= 330 °C | <= 626 °F | ||||
| Mold Temperature | >= 85.0 °C | >= 185 °F | |||
| <= 105 °C | <= 221 °F | ||||
| Drying Temperature |
100 °C @Time 21600 - 28800 sec |
212 °F @Time 6.00 - 8.00 hour |
|||
| Moisture Content | 0.100 % | 0.100 % | |||
|
De |
|||||
| Additive | Release agent | ||||
| Delivery form | Pellets | ||||
| Drying Recommended | yes | ||||
| Part Marking Code | >PA6T/66-GF35< | ISO 11469 | |||
| >PPA-GF35< | SAE J1344 | ||||
| Processing | Injection Molding | ||||
| Regional Availability | Asia Pacific | ||||
| Europe | |||||
| Global | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
| Resin Identification | PA6T/66-GF35 | ISO 1043 | |||
| Special characteristics | Heat stabilized or stable to heat | ||||
Some of the values displayed above may have been converted from their original units and/or rounded in order to display the information in a consistent format. Users requiring more precise data for scientific or engineering calculations can click on the property value to see the original value as well as raw conversions to equivalent units. We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding error. We also ask that you refer to MatWeb'sterms of use regarding this information. Click here to view all the property values for this datasheet as they were originally entered into MatWeb.
Users viewing this material also viewed the following:
DuPont Performance Polymers Zytel? HTNFR52G20NH NC010 PA6T/66-GF20FR(40)
PTS Trimid? N66-100L Lubed Nylon 6/6
Copper, UNS C26800 (Yellow brass), OSO70 Temper flat products
Applied Nanostructured Solutions PC/ABS - Carbon NanoStructure Chopped Fiber Composite
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Molded
免責(zé)聲明：（1）以上所展示的信息由企業(yè)自行提供，內(nèi)容的真實(shí)性、準(zhǔn)確性和合法性由發(fā)布企業(yè)負(fù)責(zé)，環(huán)球塑化網(wǎng)對(duì)此不承擔(dān)任何保證責(zé)任。我們?cè)瓌t上建議您優(yōu)先選擇“塑企通”會(huì)員合作! （2）同時(shí)我們鄭重提醒各位買/賣家，交易前請(qǐng)?jiān)敿?xì)核實(shí)對(duì)方身份，切勿隨意打款或發(fā)貨，謹(jǐn)防上當(dāng)受騙。如發(fā)現(xiàn)虛假信息，請(qǐng)向環(huán)球塑化網(wǎng)舉報(bào)。