SABIC Innovative Plastics Cycoloy® CX7510 PC+ABS 物性表
| 物理性能 | 額定值 (公制) | 額定值 (英制) | 測試方法 |
|---|---|---|---|
| 比重 | 1.18 g/cc | 1.18 g/cc | ASTM D 792 |
| 密度 | 1.18 g/cc | 0.0426 lb/in³ | ISO 1183 |
| 平衡吸濕 | 0.050 % | 0.050 % | 23°C / 50% RH; ISO 62 |
| 飽和吸水率 | 0.11 %
@Temperature 23.0 °C
|
0.11 %
@Temperature 73.4 °F
|
ISO 62 |
| 線性成型收縮率,Flow | 0.0056 - 0.0063 cm/cm
@Thickness 3.20 mm
|
0.0056 - 0.0063 in/in
@Thickness 0.126 in
|
SABIC Method |
| 熔體流動速率 | 16 g/10 min
@Load 2.16 kg, Temperature 260 °C
|
16 g/10 min
@Load 4.76 lb, Temperature 500 °F
|
ASTM D 1238 |
| 41 g/10 min
@Load 5.00 kg, Temperature 260 °C
|
41 g/10 min
@Load 11.0 lb, Temperature 500 °F
|
[cm^3/10 min] Melt Volume Rate; ISO 1133 | |
| 45 g/10 min
@Load 5.00 kg, Temperature 260 °C
|
45 g/10 min
@Load 11.0 lb, Temperature 500 °F
|
ASTM D 1238 |
| 機械性能 | 額定值 (公制) | 額定值 (英制) | 測試方法 |
|---|---|---|---|
| 抗張強度(斷裂) | 48.0 MPa | 6960 psi | 50 mm/min; ISO 527 |
| 49.0 MPa | 7110 psi | Type I, 50 mm/min; ASTM D 638 | |
| 抗張強度(屈服) | 64.0 MPa | 9280 psi | 50 mm/min; ISO 527 |
| 65.0 MPa | 9430 psi | Type I, 50 mm/min; ASTM D 638 | |
| 伸長率 (斷裂) | 36 % | 36 % | Type I, 50 mm/min; ASTM D 638 |
| 36 % | 36 % | 50 mm/min; ISO 527 | |
| 屈服伸長率 | 4.0 % | 4.0 % | Type I, 50 mm/min; ASTM D 638 |
| 4.5 % | 4.5 % | 50 mm/min; ISO 527 | |
| 拉伸模量 | 2.54 GPa | 368 ksi | 1 mm/min; ISO 527 |
| 2.58 GPa | 374 ksi | 50 mm/min; ASTM D 638 | |
| 彎曲強度 | 97.0 MPa | 14100 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 99.0 MPa | 14400 psi | 2 mm/min; ISO 178 | |
| 彎曲模量 | 2.33 GPa | 338 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 2.62 GPa | 380 ksi | 2 mm/min; ISO 178 | |
| 懸壁梁缺口沖擊強度 | 1.37 J/cm
@Temperature -30.0 °C
|
2.57 ft-lb/in
@Temperature -22.0 °F
|
ASTM D 256 |
| 6.40 J/cm
@Temperature 23.0 °C
|
12.0 ft-lb/in
@Temperature 73.4 °F
|
ASTM D 256 | |
| 簡支梁缺口沖擊強度 | 3.60 J/cm²
@Temperature 23.0 °C
|
17.1 ft-lb/in²
@Temperature 73.4 °F
|
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 沖擊試驗 | 65.0 J
@Temperature 23.0 °C
|
47.9 ft-lb
@Temperature 73.4 °F
|
Instrumented Impact Total Energy; ASTM D 3763 |
| 熱性能 | 額定值 (公制) | 額定值 (英制) | 測試方法 |
|---|---|---|---|
| 線形熱膨脹系數(shù) - 流動 | 69.0 µm/m-°C
@Temperature -40.0 - 40.0 °C
|
38.3 µin/in-°F
@Temperature -40.0 - 104 °F
|
ASTM E 831 |
| 72.0 µm/m-°C
@Temperature -40.0 - 40.0 °C
|
40.0 µin/in-°F
@Temperature -40.0 - 104 °F
|
ISO 11359-2 | |
| 線性熱膨脹系數(shù),橫向流動 | 72.0 µm/m-°C
@Temperature -40.0 - 40.0 °C
|
40.0 µin/in-°F
@Temperature -40.0 - 104 °F
|
ASTM E 831 |
| 75.0 µm/m-°C
@Temperature -40.0 - 40.0 °C
|
41.7 µin/in-°F
@Temperature -40.0 - 104 °F
|
ISO 11359-2 | |
| 載荷下熱變形溫度(1.8 MPa) | 95.0 °C | 203 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 106 °C
@Thickness 6.40 mm
|
223 °F
@Thickness 0.252 in
|
unannealed; ASTM D 648 | |
| 維卡軟化溫度 | 113 °C | 235 °F | Rate B/50; ASTM D 1525 |
| 115 °C | 239 °F | Rate B/50; ISO 306 | |
| 118 °C | 244 °F | Rate B/120; ISO 306 | |
| 可燃性(UL94) | V-0
@Thickness 1.50 mm
|
V-0
@Thickness 0.0591 in
|
UL 94 |
| 5VB
@Thickness 1.50 mm
|
5VB
@Thickness 0.0591 in
|
UL 94 |