PA610 美國液氮LNP LUBRICOMP QFL36 QFL-4036 物性特點: LNP加工Lubricomp * QFL36是尼龍6/10的含樹脂的玻璃纖維，聚四氟乙烯的化合物的基礎上。這種材料的新增功能包括：內(nèi)部潤滑。LNP LUBRICOMP* QFL36 is a compound based on Nylon 6/10 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
PA610 美國液氮LNP LUBRICOMP* QFL36 QFL-4036 物性數(shù)據(jù)表
|
Tensile Stress, break |
1520 |
kgf/cm² |
ASTM D 638 |
||
|
Tensile Strain, break |
2.6 |
% |
ASTM D 638 |
||
|
Tensile Modulus, 50 mm/min |
112400 |
kgf/cm² |
ASTM D 638 |
||
|
Flexural Stress |
2250 |
kgf/cm² |
ASTM D 790 |
||
|
Flexural Modulus |
86400 |
kgf/cm² |
ASTM D 790 |
||
|
Tensile Stress, break |
150 |
MPa |
ISO 527 |
||
|
Tensile Strain, break |
2.6 |
% |
ISO 527 |
||
|
Tensile Modulus, 1 mm/min |
9800 |
MPa |
ISO 527 |
||
|
Flexural Stress |
228 |
MPa |
ISO 178 |
||
|
Flexural Modulus |
9700 |
MPa |
ISO 178 |
||
|
Izod Impact, unnotched, 23°C |
95 |
cm-kgf/cm |
ASTM D 4812 |
||
|
Izod Impact, notched, 23°C |
11 |
cm-kgf/cm |
ASTM D 256 |
||
|
Instrumented Impact Energy @ peak, 23°C |
86 |
cm-kgf |
ASTM D 3763 |
||
|
Multiaxial Impact |
32 |
cm-kgf |
ISO 6603 |
||
|
Izod Impact, unnotched 80*10*4 +23°C |
65 |
kJ/m² |
ISO 180/1U |
||
|
Izod Impact, notched 80*10*4 +23°C |
12 |
kJ/m² |
ISO 180/1A |
||
|
HDT, 0.45 MPa, 3.2 mm, unannealed |
223 |
°C |
ASTM D 648 |
||
|
HDT, 1.82 MPa, 3.2mm, unannealed |
216 |
°C |
ASTM D 648 |
||
|
CTE, -40°C to 40°C, flow |
2.88E-05 |
1/°C |
ASTM E 831 |
||
|
CTE, -40°C to 40°C, xflow |
7.38E-05 |
1/°C |
ASTM E 831 |
||
|
CTE, -40°C to 40°C, flow |
2.9E-05 |
1/°C |
ISO 11359-2 |
||
|
CTE, -40°C to 40°C, xflow |
7.49E-05 |
1/°C |
ISO 11359-2 |
||
|
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm |
211 |
°C |
ISO 75/Af |
||
|
Density |
1.46 |
g/cm³ |
ASTM D 792 |
||
|
Moisture Absorption, 50% RH, 24 hrs |
0.13 |
% |
ASTM D 570 |
||
|
Mold Shrinkage, flow, 24 hrs (5) |
0.2 |
% |
ASTM D 955 |
||
|
Mold Shrinkage, xflow, 24 hrs (5) |
0.7 |
% |
ASTM D 955 |
||
|
Mold Shrinkage, flow, 24 hrs (5) |
0.17 |
% |
ISO 294 |
||
|
Mold Shrinkage, xflow, 24 hrs (5) |
0.7 |
% |
ISO 294 |
||
|
Drying Temperature |
80 |
°C |
|||
|
Drying Time |
4 |
hrs |
|||
|
Maximum Moisture Content |
0.12 - 0.2 |
% |
|||
|
Melt Temperature |
270 - 275 |
°C |
|||
|
Front - Zone 3 Temperature |
270 - 280 |
°C |
|||
|
Middle - Zone 2 Temperature |
260 - 270 |
°C |
|||
|
Rear - Zone 1 Temperature |
250 - 260 |
°C |
|||
|
Mold Temperature |
80 - 95 |
°C |
|||
|
Back Pressure |
0.2 - 0.3 |
MPa |
|||
|
Screw Speed |
30 - 60 |
rpm |
|||
PA610 美國液氮LNP LUBRICOMP* QFL36 QFL-4036 注塑參數(shù):
|
注塑成型 |
值 |
單位 |
|
干燥溫度 |
80 |
°C |
|
干燥時間 |
4 |
小時 |
|
大水分含量 |
0.12 - 0.2 |
％ |
|
熔體溫度 |
270 - 275 |
°C |
|
接待 - 第3區(qū)的溫度 |
270 - 280 |
°C |
|
中東 - 第2區(qū)溫度 |
260 - 270 |
°C |
|
后 - 1區(qū)溫度 |
250 - 260 |
°C |
|
模具溫度 |
80 - 95 |
°C |
|
背壓 |
0.2 - 0.3 |
兆帕 |
|
螺桿轉速 |
30 - 60 |
轉 |
東莞市鼎鑫塑化公司銷售美國液氮PA610尼龍系列產(chǎn)品:
|
PA610 |
美國液氮 |
PDX-98071 |
|
PA610 |
美國液氮 |
QC-1002HS BK |
|
PA610 |
美國液氮 |
QCL-4036 BK |
|
PA610 |
美國液氮 |
QF-100-10 |
|
PA610 |
美國液氮 |
QF-1006 BK |
|
PA610 |
美國液氮 |
QF-1006FR |
|
PA610 |
美國液氮 |
QFL-4017 |
|
PA610 |
美國液氮 |
QFL-4036 |
|
PA610 |
美國液氮 |
QL4040 NT92 |
|
PA610 |
美國液氮 |
QL4540 |
|
PA610 |
美國液氮 |
QP004 |
|
PA610 |
美國液氮 |
QP1004 |
免費提供PA610 美國液氮LNP LUBRICOMP QFL36 QFL-4036 以上產(chǎn)品詳細物性數(shù)據(jù)表\UL黃卡\注塑參數(shù)\MSDS及新報價,訂購電話:13929209907文生 或QQ 772681812